Product Description産品描述
Lead-free migration resistant PVC compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
環保型聚氯乙烯耐遷移料是以優質聚氯乙烯樹脂爲基料,加入特種增塑劑、特種穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
 
Characteristics and Application 特點及用途
The products have excellent migration-resistant properties and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of wire and cables which have anti-PS or anti-ABS property requirements.
産品具有良好的非遷移性,加工性能優異,符合RoHS環保標准。主要用于耐PS或ABS電線電纜絕緣和護套。
 
Processing Indicator加工工藝
Recommend to use single-screw extruders with L/D= 20-25.
建議使用普通長徑比爲20-25的單螺杆擠出機進行生産。
Model
牌號
Machine Barrel Temperature
機筒溫度
Molding Temperature
機頭溫度
W-7091 / W-9091 / W-0591 150-175℃ 170-185℃
W-7092 / W-9092 / W-0592 150-175℃ 170-180℃
 
 
Physical and Electrical Properties
機械物理性能及電性能指標

Item

試驗項目

Unit
單位
Technical Requirements
技術要求
W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
Tensile Strength
拉伸強度
MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
Elongation at Break
斷裂伸長率
% ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
Thermal Deformation
熱變形
% ≤40 ≤50 ≤40 ≤50 ≤40 ≤50
Brittle Temperature with Impact
沖擊脆化溫度
-15 -20 -15 -20 -15 -20
200℃Thermal Stability
200℃時熱穩定時間
min ≥60 ≥60 ≥80 ≥80 ≥80 ≥80
20℃Volume Resistivity
20℃時體積電阻率
Ω.m ≥1.0×1011 ≥1.0×108 ≥1.0×1011 ≥1.0×109 ≥1.0×1011 ≥1.0×109
Dielectric Strength
介電強度
MV/m ≥20 ≥18 ≥20 ≥18 ≥20 ≥18
Thermal Aging
熱老化試驗
\ 100℃×168h 100℃×168h 100℃×240h 100℃×240h 135℃×168h 135℃×168h
Tensile strength after aging
老化后拉伸強度
MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
Tensile Strength Variation
拉伸強度变化率
% ±20 ±20 ±20 ±20 ±20 ±20
Elongation After Aging
老化后斷裂伸長率
% ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
Elongation Variation
斷裂伸長率变化率
% ±20 ±20 ±20 ±20 ±20 ±20
Migration ResistantTest
耐遷移試驗
(55℃×168h)
\ 無汙染 無汙染 無汙染 無汙染 無汙染 無汙染