环保型105℃汽车原线料 W-0598A
105℃ Lead-free Automotive Wire Compound...
型號:0

參考價:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Product description 産品描述
105℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients.
環保型105℃汽車原線料是以優質聚氯乙烯樹脂爲基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
 
Characteristics and Application 特點及用途
These products have excellent mechanical and physical properties, electrical property and good processability. They can meet RoHS Standard. Their AVS cables can meet JASO D 611 Standards and other related standards. The highest working temperature is 105℃.
产品具有良好的机械物理性能和电性能,加工性能优异,符合RoHS环保标准。该产品制作的AVSS电线可满足JASO D 611等相关标准,最高工作温度为105℃。
 
Processing Indicator 加工工藝
Recommend to use single-screw extruders with L/D= 20-25.
建議使用普通長徑比爲20-25的單螺杆擠出機進行生産。
Model
牌號
Machine Barrel Temperature
機筒溫度
Molding Temperature
機頭溫度
W-0598A 165-185℃ 185-190℃
 

 
Physical and Electrical Properties 機械物理性能及電性能指標

Item

試驗項目

Unit
單位
Technical Requirements
技術要求
Density
比重
\ 1.32±0.02
Tensile Strength
拉伸強度
MPa ≥18.0
Elongation at Break
斷裂伸長率
% ≥250
200℃Thermal Stability
200℃時熱穩定時間
min ≥200
Brittle Temperature with Impact
沖擊脆化溫度
-20
20℃Volume Resistivity
20℃時體積電阻率
Ω.m ≥1×1011
Hardness
硬度
Shore A 94±2
Thermal Aging
熱老化試驗
\ 136℃×168h
Tensile Strength Variation
拉伸強度变化率
% ±25
Elongation Variation
斷裂伸長率变化率
% ±25