环保型125℃汽车原线料 W-2597, W-2598
125℃ Lead-free Automotive Wire Compound...
型號:0

參考價:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Product Description 産品描述
125℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients. These products have excellent mechanical and physical properties, electrical property and good processability. They can meet RoHS Standard. The cables with them can meet T3 automotive wire requirements in NFR13-415 standards. The highest working temperature is 125℃.
环保型125℃汽车原线料是以优质聚氯乙烯树脂为基料,加入特种增塑剂、稳定剂等助剂,经混合、塑化、造粒而成的粒状电缆料。产品具有良好的机械物理性能和电性能,加工性能优异,符合RoHS环保标准。制成电线后可满足ISO 6722 中T3型汽车线要求,最高工作温度为125℃。
 
Product Details 産品明細
Model
牌號
Application
用途
W-2597 >0.5mm2 cables
0.5mm2以上規格的電線
W-2598 ≤ 0.5mm2 cables
0.5mm2及以下規格的電線
 
 
 
 
Processing Indicator 加工工藝
Recommend to use single-screw extruders with L/D= 20-25.
建議使用普通長徑比爲20-25的單螺杆擠出機進行生産。
Model
牌號
Machine Barrel Temperature
機筒溫度
Molding Temperature
機頭溫度
W-2597 165-185℃ 180-190℃
W-2598 165-185℃ 185-195℃
 
 
Physical and Electrical Properties 機械物理性能及電性能指標

Item

試驗項目

Unit
單位
Technical Requirements
技術要求
W-2597 W-2598
Density
比重
\ 1.34±0.02 1.34±0.02
Tensile Strength
拉伸強度
MPa ≥18.0 ≥18.0
Elongation at Break
斷裂伸長率
% ≥150 ≥150
200℃Thermal Stability
200℃時熱穩定時間
min ≥360 ≥360
20℃Volume Resistivity
20℃時體積電阻率
Ω.m ≥1×1011 ≥1×1011
Brittle Temperature with Impact
沖擊脆化溫度
-25 -25
Hardness
硬度
Shore A 94±2 97±2
Thermal Aging
熱老化試驗
\ 155±3℃×240h
Tensile Strength Variation
拉伸強度变化率
% ±20 ±20
Elongation Variation
斷裂伸長率变化率
% ±20 ±20