您所在的位置:網站首頁 > > 産品中心 > XLPE絕緣材料 > 低煙無鹵電纜料70℃热塑性低烟无卤阻燃护套料 EHW70,EHW70C,EHW70A
70℃热塑性低烟无卤阻燃护套料 EHW70,EHW70C,EHW70A
70℃ Thermoplastic Low-smoke Halogen-free Flame-retardant Jacketing Compound. ...
型號:0

參考價:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Description and Application  産品描述和用途
EHW70, EHW70C, EHW70A are thermoplastic low-smoke halogen-free jacketing compound, which don’t contain any heavy metal like Pb, Ba, Cd, Cr, Sn and Sb. The properties can meet RoHS Standard. They have excellent mechanical and flame-retardant properties with temperature resistant from -40℃to 70℃. They are mainly used for the jacketing of communication cables, control cables and power cables.
EHW70,EHW70C,EHW70A是熱塑性低煙無鹵護套料。不含Pb、Ba、Cd、Cr、Sn、Sb六大重金屬。其性能均能滿足RoHS的標准要求。具有優異的物理機械性能和阻燃性能,可耐溫-40℃~70℃,主要用于通信電纜,控制電纜和電力電纜的護套層。
 

Processing Indicator   加工工藝
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低煙無鹵專用螺杆,長徑比L/D=20-25。
Model
牌號
Machine Barrel Temperature
機筒溫度
Molding Temprature
機頭溫度
EHW70/EHW70C/EHW70A 130-140℃ 150-160℃
 
 
Physical and Electrical Properties   物理及電性能指標
Item
試驗項目
Unit
單位
Specification
技術要求
EHW70 EHW70C EHW70A
Density
密度
g/cm3 ≤1.5 ≤1.5 ≤1.55
Tensile Strength
拉伸強度
MPa ≥10 ≥10 ≥10
Elongation at Break
斷裂伸長率
% ≥150 ≥150 ≥150
Aging Conditions
熱老化條件
/ 100℃×168h
Tensile Strength Variation
拉伸強度变化率
% ±25 ±25 ±25
Elongation Variation
斷裂伸長率变化率
% ±25 ±25 ±25
Thermal
Deformation
熱變形
Condition 70℃×6h
Variation % ≤50 ≤50 ≤50
Dielectric Strength
介電強度
MV/m ≥20 ≥20 ≥20
Brittle Temperature With Low Temperature Impact
沖擊脆化溫度
-40 -40 -40
20℃Volume Resistivity
20℃體積電阻率
Ω.m ≥1.0×1011 ≥1.0×1011 ≥1.0×1011
Water Absorption吸水性实验
14 days at 70℃
mg/cm2 ≤5 ≤5 ≤5
Oxygen Index
氧指數
% ≥32 ≥36 ≥38
HCL Gas Evolution
HCL氣體發生量
Mg/g ≤1.0 ≤1.0 ≤1.0
PH Value
PH值
/ ≥4.3 ≥4.3 ≥4.3
Smoke Density烟密度
– No-flame Mode无焰模式
– Flame Mode有焰模式
Ds max  
≤200
≤100
 
≤200
≤100
 
≤200
≤100
Conductivity
電導率
uS/mm ≤10 ≤10 ≤10
Toxicity Index
毒性指數
/ ≤5.0 ≤5.0 ≤5.0
 
 
Attentions 注意事項:
1)The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘幹後才能使用,材料一經開封,建議12小時之內用完。
2)Please ensure the screw, barrel, hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前確保螺杆、機筒、加料鬥徹底清理幹淨,加工過程中嚴禁帶入雜質。
3)If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速擠出時,請慢慢逐漸加快螺杆轉速,以免塑化不良,電纜表面毛糙。